КОМПОЗИЦИОННЫЕ ЭЛЕКТРОХИМИЧЕСКИЕ ПОКРЫТИЯ НА ОСНОВЕ СПЛАВА НИКЕЛЬ — ХРОМ: ПОЛУЧЕНИЕ И СВОЙСТВА

Vitalii N. Tseluikin; Ekaterina A. Vasilenko; Olga G. Nevernay; Galina V. Tseluikina; Vladimir A. Denisov

Authors

Vitalii N. Tseluikin grand PhD (Eng.), professor of Physical and Organic Chemistry Department, Engels Technological Institute (Branch) of Saratov State Technical University; e-mail: tseluikin@mail.ru
Ekaterina A. Vasilenko the post graduate student of Physical and Organic Chemistry Department, Engels Technological Institute (Branch) of Saratov State Technical University
Olga G. Nevernay PhD (Chem.), associate professor of Physical and Organic Chemistry Department, Engels Technological Institute (Branch) of Saratov State Technical University
Galina V. Tseluikina PhD (Eng.), associate professor of Technology of Electrochemical Productions Department, Engels Institute of Technology (Branch), Saratov State Technical University.
Vladimir A. Denisov assistant of Machinery and Equipment for the Chemical Industry Department, Engels Institute of Technology (Branch), Saratov State Technical University

Keywords:

композиционные электрохимические покрытия, сплав никель — хром, бисульфат графита, коэффициент трения скольжения, микротвердость.

Abstract

Получены композиционные электрохимические покрытия (КЭП) на основе сплава никель — хром, содержащие бисульфат графита в качестве дисперсной фазы. Установлено, что коэффициенты трения скольжения КЭП никель — хром — бисульфат графита уменьшаются по сравнению с аналогичными покрытиями без дисперсной фазы. Изучено влияние катодной плотности тока на микротвердость осадков сплава никель — хром.