МАГНИТНАЯ ФАЗОВАЯ ДИАГРАММА ТВЕРДЫХ РАСТВОРОВ Fe1–xZnxCr2S4

Telman G. Aminov; Galina G. Shabunina; Denis I. Kirdyankin; Oleg E. Myslitskii; Vladimir M. Novotorcev

Authors

Telman G. Aminov grand PhD (Chem.), professor of Kurnakov Institute of General and Inorganic Chemistry, RAS; tel.: (495) 9543841, e-mail: aminov@igic.ras.ru
Galina G. Shabunina grand PhD (Chem.), senior scientific employee of Kurnakov Institute of General and Inorganic Chemistry, RAS; tel.: (495) 9543841, e-mail: info@igic.ras.ru
Denis I. Kirdyankin PhD (Chem.), scientific employee of Kurnakov Institute of General and Inorganic Chemistry, RAS; tel.: (495) 9543841, e-mail: info@igic.ras.ru
Oleg E. Myslitskii lead engineer of Kurnakov Institute of General and Inorganic Chemistry, RAS; tel.: (495) 9543841, e-mail: info@igic.ras.ru
Vladimir M. Novotorcev grand PhD (Chem.), Academician, RAS, director of Kurnakov Institute of General and Inorganic Chemistry, RAS; tel(495) 9520224, e-mail: vmnov@igic.ras.ru

Keywords:

магнитный полупроводник, спиновое стекло.

Abstract

Установлены температурные и концентрационные границы областей существования магнитно активных фаз на основе ферримагнетика FeCr2S4 (0 ≤ х ≤ 0.63), антиферромагнетика ZnCr2S4 (0.73 ≤ х ≤ 1) и спинового стекла (0.63 ≤ х ≤ 0.73), обладающих структурой шпинели. Экспериментально и теоретически изучены концентрационные зависимости магнитного момента насыщения и температуры Кюри синтезированных твердых растворов.