МОДИФИКАЦИЯ ПЛЕНКИ СЕЛЕНИДА СВИНЦА ПУТЕМ ВЫДЕРЖКИ В РАСТВОРЕ СОЛИ ОЛОВА (II)

Zinaida I. Smirnova; Vyacheslav F. Markov; Larisa N. Maskaeva; Vladimir I. Voronin; Mikhail V. Kuznetsov

Authors

Zinaida I. Smirnova post-graduate stu dent, Ural Federal University named after the first President of Russia B.N. Yeltsin; tel.: (343) 3759318, e-mail: imsok@bk.ru
Vyacheslav F. Markov grand PhD (Chem. ), professor, Ural Federal University named after the first President of Russia B.N. Yeltsin; tel.: (343) 3759318, e-mail: markv@mail.u stu. ru
Larisa N. Maskaeva grand PhD (Chem. ), professor, Ural Federal University named after the first President of Russia B.N. Yeltsin; tel.: (343) 3759318, e-mail: mln@e-sky. ru
Vladimir I. Voronin PhD (Phys.-Math.), senior researcher, Institut e of Metal Physics, Ural Branch, RAS; tel.: (343) 3759318, e-mail: markv@mail.u stu. ru
Mikhail V. Kuznetsov grand PhD (Chem. ), chief researcher, Institut e of Solid State Chemistry, Ural Branch, RAS; tel.: (343) 3759318, e-mail: kuznetsov@mail.u ran.ru

Keywords:

селенид свинца, тонкие пленки, модификация поверхности, гидрохимическое осаждение, адсорбция из раствора.

Abstract

Методами рентгеновской дифракции и рентгеновской фотоэлектронной спектроскопии при послойном травлении исследованы тонкие поликристаллические пленки PbSe после выдержки в растворе хлорида олова(II) при температуре 353К. Выполнено концентрационное профилирование слоев пленки толщиной до ~21 нм, определены основные химические формы элементов на ее поверхности. Показано, что контакт «пленка PbSe — водный раствор SnCl2» приводит к вхождению олова в поверхностные слои базового материала при одновременном понижении степени совершенства его кристаллической структуры.