КРИСТАЛЛИЗАЦИЯ И ТЕМПЕРАТУРНАЯ ЗАВИСИМОСТЬ ЭЛЕКТРОСОПРОТИВЛЕНИЯ МАССИВНОГО МЕТАЛЛИЧЕСКОГО СТЕКЛА Zr46Cu46Al8

Andrey S. Makarov; Svetlana V. Khonik; Vitaly A. Khonik; Natalia A. Divakova; Gennady V. Afonin

Authors

Andrey S. Makarov master student of solid state physics department, Voronezh State University; tel.: (908) 1351407, e-mail: a.s.makarov.vrn@gmail.com
Svetlana V. Khonik PhD (physical and mathematical sciences), senior staff scientist, Voronezh State University; tel.: (951) 5638617, e-mail: skhonik@mail.ru
Vitaly A. Khonik grand PhD (physical and mathematical sciences), professor, department of general physics, Voronezh State Pedagogical University, department of experimental physics, Voronezh State University; tel.: (473) 2390433, e-mail: khonik@ac.vspu.ru
Natalia A. Divakova PhD (chemistry sciences), senior staff scientist, Tecnopark, Voronezh State University; tel.: (473) 2208445, e-mail: nada@mail.ru
Gennady V. Afonin post-graduate student, department of general physics, Voronezh State Pedagogical University; tel.: (473) 2390433, e-mail: afoningv@gmail.com

Keywords:

металлические стекла, электросопротивление, кристаллизация.

Abstract

Проведено исследование температурной зависимости электросопротивления массивного металлического стекла Zr46Cu46Al8 в интервале от комнатной температуры до 873 К. Показано, что на температурной зависимости электросопротивления металлического стекла
Zr46Cu46Al8 хорошо идентифицируются состояние переохлажденной жидкости и последующая продолжительная кристаллизация. Рентгеноструктурные исследования подтвердили длительный многостадийный кристаллизационный процесс исследуемого металлического стекла.