ВЛИЯНИЕ ОТЖИГА НА ФАЗОВЫЙ СОСТАВ ПЛЕНОК CuInSe2, ПОЛУЧАЕМЫХ МЕТОДОМ ЭЛЕКТРОХИМИЧЕСКОГО ОСАЖДЕНИЯ

Mikhail V. Gapanovich; Svetlana I. Bocharova; Gennadii F. Novikov; Vasilina A. Sergeeva; Ivan N. Odin

Authors

Mikhail V. Gapanovich scientifi c employee, Institute of problems of chemical physics Russian academy of science; tel.: (496) 5221842, e-mail: gmw@icp.ac.ru
Svetlana I. Bocharova the post-graduate student, the engineer, Institute of problems of chemical physics Russian academy of science; tel.: (496) 5221793, e-mail: sveta7@ icp.ac.ru
Gennadii F. Novikov managing laboratory, Institute of problems of chemical physics Russian academy of science; tel.: (496) 5221842, e-mail: ngf@icp.ac.ru
Vasilina A. Sergeeva the student, department of basic physical chemistry engineering, Moscow State University; e-mail: tracytheplane@mail.ru
Ivan N. Odin senior scientifi c employee, department of chemistry, Moscow State University; e-mail: inodin@ inorg.chem.msu.ru

Keywords:

CIS, тонкие пленки, электрохимическое осаждение, отжиг.

Abstract

Пленки CuInSe2, используемые в качестве поглощающих слоев в преобразователях солнечной энергии, синтезировали методом электрохимического осаждения из спиртовых растворов в области потенциалов от –1200 до –800 мВ. Получаемые пленки состояли из наночастиц со средним диаметром менее 10 нм. Фазовый состав пленок зависел от условий осаждения CuInSe2. Для получения однофазных микрокристаллических пленок принципиально важным оказался дополнительный отжиг пленок в парах селена