СИНТЕЗ НАНОПОРОШКОВ La1–xSr(Са)xFeO3 (х = 0; 0.1; 0.2; 0.3) ЗОЛЬ-ГЕЛЬ МЕТОДОМ

Nguyen Anh Tien; V. O. Mittova; Dinh Van Tac; I. Ya. Mittova

Authors

Nguyen Anh Tien PhD, Physical Chemistry Department, Ho Chi Minh City University of Pedagogy, Ho Chi Minh City, Vietnam
V. O. Mittova Ph.D., Biochemistry Department, Voronezh Medical Academy, Voronezh; email: vmittova@ mail.ru
Dinh Van Tac Ph.D. student of Department of Material Science and Industry of Nanosystems, Voronezh State University; email: dinhvantac@yandex.ru
I. Ya. Mittova grand PhD, professor, doctor of chemical sciences, Department of Material Science and Industry of Nanosystems, Voronezh State University, Voronezh City, Russia; email: inorg@chem.vsu.ru

Keywords:

золь-гель метод, нанопорошки, ферриты, La1–xSr(Са)xFeO3 (х = 0.1; 0.2; 0.3).

Abstract

Методом соосаждения катионов La3+, Sr2+(Ca2+) и Fe3+ водным раствором аммиака и карбоната натрия осуществлен синтез нанопорошков ферритов La1–xSr(Са)xFeO3 (х = 0.1; 0.2; 0.3). Полученные образцы исследованы методами рентгенофазового анализа, просвечивающей электронной микроскопии и локального рентгеноспектрального микроанализа. Размер частиц полученных порошков после отжига при 950° С в течение 1ч не превышает 70 нм.