СИНТЕЗ НАНОКРИСТАЛЛИЧЕСКИХ ТВЕРДЫХ РАСТВОРОВ НА ОСНОВЕ ДИОКСИДА ЦЕРИЯ, ДОПИРОВАННОГО РЗЭ

Olga S. Polezhaeva; Vladimir K. Ivanov; Ekaterina A. Dolgopolova; Alexander E. Baranchikov; Yuri D. Tretyakov

Authors

Olga S. Polezhaeva researcher, Kurnakov Institute of General and Inorganic Chemistry RAS, tel.: (495) 6338534; е-mail: polezhaeva.olga@gmail.com
Vladimir K. Ivanov leading scientifi c employee, Kurnakov Institute of General and Inorganic Chemistry RAS; tel.: (495) 6338534; е-mail: van@igic.ras.ru
Ekaterina A. Dolgopolova student, Department of Material Science, Moscow State University; tel.: (495) 6338534
Alexander E. Baranchikov senior researcher, Kurnakov Institute of General and Inorganic Chemistry RAS; tel.: (495) 6338534; e-mail: a.baranchikov@yandex.ru
Yuri D. Tretyakov chief of the Department of Inorganic Chemistry, Department of Material Science, Moscow State University; tel.: (495) 9392074; e-mail: yudt@inorg. chem.msu.ru

Keywords:

гомогенный гидролиз, диоксид церия, твердые растворы, параметр кристаллической решетки, .

Abstract

Методом гомогенного гидролиза в присутствии гексаметилентетрамина получены нанокристаллические (<10 нм) твердые растворы на основе диоксида церия, допированные РЗЭ (Pr, Nd, Sm, Eu, Yb) в различной концентрации (5—20 мол. %). Установлено, что увеличение концентрации допантов от 0 до 20 мольных процентов приводит к значительному уменьшению размеров частиц (от ~ 7 вплоть до 4 нм), а также к линейному изменению параметра кристаллической решетки в соответствии с законом Вегарда.