СРАВНИТЕЛЬНЫЙ АНАЛИЗ СОСТАВА И МОРФОЛОГИИ ПОВЕРХНОСТИ ТЕРМООБРАБОТАННЫХ СТРУКТУР ГА/Тi И ГА/TiO2/Тi

Anastasiya U. Berezhnaya; Valentina O. Mittova; Irina Ya. Mittova; Alexander V. Kostyuchenko

Authors

Anastasiya U. Berezhnaya the post-graduate student; chair of Material Science and Industry of Nanosystems, Voronezh State University; tel.: (4732) 232437, e-mail: bau_xxx@mail.ru
Valentina O. Mittova PhD (biological sciences), chair of Voronezh State Medical academy named after N.N. Burdenko; tel.: (4732) 530338, e-mail: vmittova@mail.ru
Irina Ya. Mittova grand PhD (chemistry sciences), professor, chair of Material Science and Industry of Nanosystems, Voronezh State University; tel.: (4732) 208356, email: inorg@chem.vsu.ru
Alexander V. Kostyuchenko PhD (physical and mathematical sciences), assistant chair of Material Science and Industry of Nanosystems, Voronezh State University; tel.: (920) 2124561, e-mail: av-kostuchenko@mail.ru

Keywords:

гидроксиапатит, титан, оксид титана, тонкие пленки, многослойные структуры, биоактивность.

Abstract

В работе представлены данные сравнительного анализа структур ГА/Тi и ГА/TiO2/Тi при высокотемпературном отжиге в аргоне. Показано, что разложение гидроксиапатита (ГА) происходит при более низких температурах (от 900 °C для структур ГА/Тi и от 950 °C для
структур ГА/ТiO2/Тi), чем ранее упоминалось в литературе (1150—1200 °C). При отжиге обнаружено окисление титана до субоксидов, причем на этот процесс расходуется кислород из пленки ГА. Установлено, что высокотемпературная обработка образцов способствует повышению биосовместимости имплантатов на основе ГА и титана.